ASTM A Standard Specification for Steel Strip, High Carbon, Cold Rolled, General Requirements. Find the most up-to-date version of ASTM A at Engineering ASTM A, AM – Designation: A /A M – 02 An American National Standard Standard Spe.

Author: Mik Kazijas
Country: Tajikistan
Language: English (Spanish)
Genre: Business
Published (Last): 14 November 2017
Pages: 147
PDF File Size: 20.7 Mb
ePub File Size: 13.77 Mb
ISBN: 448-5-40250-377-7
Downloads: 67764
Price: Free* [*Free Regsitration Required]
Uploader: Meztikus

Government procurement by the Defense Supply Agency, strip material shall be continuously marked for identi? General Requirements for Delivery 4. ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard.

However, unless the order specifies the applicable “M” specification designation SI unitsthe material shall be furnished to inch-pound units. The elements comprising the desired chemical composition are speci? NOTE 2—The industry de? Originally published as A — Conformance to SI tolerances is mandatory when the “M” specification is used. ashm

ASTM A682 Grade 1074

Strip is classified as product that is 0. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. Thickness Tolerances Plus or Minus, in. Combining values from the two systems will result in nonconformance with the speci? The values listed are not exact conversions of the values listed in the inch-pound tables but instead are rounded or rationalized values.

Unless otherwise agreed to, all tests and inspections, a628 product analysis, shall be made at the place of production.

Elements such as aluminum may be added in sufficient amounts to control the austenitic grain size. Current edition approved March 10, This standard is subject to revision at any time by the responsible technical committee and must be reviewed every? A superscript epsilon e indicates an editorial change since the last revision or reapproval. Conformance to SI tolerances is mandatory when the “M” specification is used. B Measured 10 mm or more in from edge; and on narrower than 25 mm, at any place between edges.

  ERIC RENNER PINHOLE PHOTOGRAPHY PDF

Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. The results of analyses taken from different pieces within a heat may differ from each other and from the cast analysis. When one or more of these elements is speci?

Link to Active This link will always route to the current Active version of the standard. The material must be adequately protected and correctly identi?

The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. NOTE 3—When the camber tolerances shown in Table 8 are not suitable for a particular purpose, cold-rolled strip is sometimes machine straightened.

B The sum of copper, nickel, chromium, and molybdenum shall not exceed 0.

ASTM A, AM_百度文库

Strip is classified as product that is 0. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other.

Number of Tests and Retests sstm However, under SI the preferred term in mass. In case of dissatisfaction with the results of the test, the manufacturer may make claims for a rehearing. NOTE 2—Camber tolerances as shown in the table are for any mm length.

  ELECTROTHERMAL IA9100 PDF

Finish and Edges When the maximum manganese limit exceeds 1. Rework and Retreatment S682 1—The term weight is used when inch-pound units are the standard.

The values listed are not exact conversions of the values listed in the inch-pound tables but instead are rounded or rationalized values. Two additional samples are secured from each end of the coil from which the original sample was taken.

Within the text, the SI units are shown in brackets. Over 12 Width Tolerance, Plus and Minus, in. When the amount of vanadium, columbium, or titanium is less than 0. Each of the elements listed in Tables 2 and 3 and additional elements agreed upon by the purchaser and the supplier shall be included in aa682 report of heat analysis. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility.

A portion of the coil may be discarded prior to cutting the samples for retest.

C When the chromium is speci? Rejection and Rehearing Notwithstanding the absence of a signature, the organization submitting the document is responsible for the content of the document. However, under SI the preferred term in mass.